OA 66AL
About this product
One-part, 100% solid, UV curable bonding adhesive
Application Method
Dispensing
,
Curing Conditions
Few seconds with UV (365nm, 2 - 5W/cm²)
Thermal cure at 90-100°C for 30 minutes if necessary.
Viscosity
0.3-0.5 Kcp
C.T.E
65 ppm/°C
Reflow Temperature
N/A
features
Cost-effective solutions, built for scale
01
High throughput & process yield
Maintains mechanical and chemical stability during high-temperature assembly processes, including Pb-free reflow profiles and prolonged thermal exposure.
02
Low thermal stress
Engineered to achieve reliable adhesion across common PCB substrates, reducing the risk of delamination during thermal cycling and operational stress.
03
Excellent moisture resistance
Formulated to minimise mechanical stress at the solder joint interface, helping to mitigate fatigue and micro-cracking over the product’s operational lifetime.
benefits
Designed for Long-Term Reliability
01
Provides bubble free optical coverage after cure
Enhances solder joint durability under repeated thermal cycling and mechanical loading, supporting long-term performance in demanding environments.
02
Forms a very flexible bond
Lowers the likelihood of mechanical and thermal failure in high-temperature and high-density assemblies, improving overall system robustness.
03
Forms a very flexible bond
Supports stable, repeatable production outcomes by reducing process variability and material-related defects across manufacturing runs.
downloadables
Technical Documentation
Technical Datasheet (TDS)
File type
PDF
Date Uploaded
Apr 2026
Size
333kb
Safety Data Sheet (SDS)
File type
PDF
Date Uploaded
Apr 2026
Size
303kb
Innovation At Its Best
Engineering Materials for Micro-Chip Applications
.svg)
.svg)