SMT 138E
About this product
Conductive, rapid-cure, self-leveling and self-soldering adhesive
Application Method
Dispensing
,
Curing Conditions
Ambient to peak temperature time to be 4-5 minutes with peak temperature from 140-190°C
Viscosity
50-100 Kcp
C.T.E
23.5 ppm/°C
Reflow Temperature
140-190°C for reflow
features
Cost-effective solutions, built for scale
01
Excellent electrical conductivity
Maintains mechanical and chemical stability during high-temperature assembly processes, including Pb-free reflow profiles and prolonged thermal exposure.
02
Eliminates contact resistance
Engineered to achieve reliable adhesion across common PCB substrates, reducing the risk of delamination during thermal cycling and operational stress.
03
Low temperature soldering application
Formulated to minimise mechanical stress at the solder joint interface, helping to mitigate fatigue and micro-cracking over the product’s operational lifetime.
benefits
Designed for Long-Term Reliability
01
Eliminates out gassing from soldering process
Enhances solder joint durability under repeated thermal cycling and mechanical loading, supporting long-term performance in demanding environments.
02
Eliminates flux residue
Lowers the likelihood of mechanical and thermal failure in high-temperature and high-density assemblies, improving overall system robustness.
03
Eliminates flux residue
Supports stable, repeatable production outcomes by reducing process variability and material-related defects across manufacturing runs.
downloadables
Technical Documentation
Technical Datasheet (TDS)
File type
PDF
Date Uploaded
Apr 2026
Size
333kb
Safety Data Sheet (SDS)
File type
PDF
Date Uploaded
Apr 2026
Size
303kb
Innovation At Its Best
Engineering Materials for Micro-Chip Applications
.svg)
.svg)